現(xiàn)貨供應(yīng) ABS/PC 基礎(chǔ)創(chuàng)新塑料(美國) DL100 BK1743U
DL100 NA1001 BK1743U
CYCOLAC DL100 is a high heat, high impact, low emissions ABS/PC blend.EUROPEASIAAMERICAS
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yield, 5 mm/min | 46 | MPa | ISO 527 | |
| Tensile Stress, yield, 50 mm/min | 45 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3.5 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 60 | % | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 3.4 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 10 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2200 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 69 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2250 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 91 | MPa | ISO 2039-1 | |
| IMPACT | ||||
| Izod Impact, notched 80*10*4 +23°C | 35 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 34 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 14 | kJ/m2 | ISO 179/1eA | |
| THERMAL | ||||
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 | |
| CTE, 23°C to 60°C, flow | 9.8E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 9.8E-05 | 1/°C | ISO 11359-2 | |
| Vicat Softening Temp, Rate B/50 | 105 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 107 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 104 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 87 | °C | ISO 75/Ae | |
| Relative Temp Index, Elec | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B | |
| PHYSICAL | ||||
| Mold Shrinkage on Tensile Bar, flow | 0.5-0.7 | % | SABIC method | |
| Density | 1.08 | g/cm3 | ISO 1183 | |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 8 | cm3/10 min | ISO 1133 | |
| FLAME CHARACTERISTICS | ||||
| UL Yellow Card | E45329-236566 | - | - | |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 90-100 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Maximum Moisture Content | 0.1 | % | ||
| Melt Temperature | 250-280 | °C | ||
| Nozzle Temperature | 245-275 | °C | ||
| Front - Zone 3 Temperature | 250-280 | °C | ||
| Middle - Zone 2 Temperature | 250-280 | °C | ||
| Rear - Zone 1 Temperature | 230-260 | °C | ||
| Hopper Temperature | 60-80 | °C | ||
| Mold Temperature | 40-80 | °C |