點(diǎn)擊圖片查看大圖
產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 比重 |
|
ASTM D792,ISO 1183 | 1.53 | g/cm3; |
|
|
熔流率 | 250°C/2.16 kg | ASTM D1238 | 16 | g/10min |
|
|
收縮率 | 流動 | ASTM D955 | 0.30-0.50 | % |
|
|
|
橫向流量 | ISO 294-4 | 0.70-1.1 | % |
|
|
|
流量 | ISO 294-4 | 0.30-0.70 | % |
|
|
吸水率 | 平衡, 23°C, 50% RH | ISO 62 | 0.20 | % |
|
|
粘數(shù) |
|
ISO 307 | 74.0 |
cm3;/g
|
|
|
洛氏硬度 | M 計(jì)秤 | ISO 2039-2 | 90 |
|
| 機(jī)械性能 | 拉伸模量 | -40°C | ASTM D638 | 11000 | MPa |
|
|
|
-4°C | ASTM D638 | 10500 | MPa |
|
|
|
0°C | ASTM D638 | 9650 | MPa |
|
|
|
23°C | ASTM D638 | 4830 | MPa |
|
|
|
80°C | ASTM D638 | 3760 | MPa |
|
|
|
--
|
ISO 527-2/1A/1 | 9200 | MPa |
|
|
抗張強(qiáng)度 |
斷裂, -40°C
|
ASTM D638 | 190 | MPa |
|
|
|
斷裂, 0°C
|
ASTM D638 | 159 | MPa |
|
|
|
斷裂, 23°C | ASTM D638 | 134 | ? MPa |
|
|
|
斷裂, 80°C | ASTM D638 | 77.6 | MPa |
|
|
|
斷裂, 121°C | ASTM D638 | 61.4 | MPa |
|
|
|
斷裂 | ISO 527-2/1A/5 | 130 | ? MPa |
|
|
伸長率 |
斷裂, -40°C
|
ASTM D638 | 1.9 | ? % |
|
|
|
斷裂, 0°C
|
ASTM D638 | 1.9 | ? % |
|
|
|
斷裂, 23°C | ASTM D638 | 2.0 | ? % |
|
|
|
斷裂, 80°C | ASTM D638 | 3.9 | ? % |
|
|
|
斷裂, 121°C | ASTM D638 | 4.3 | % |
|
|
|
斷裂 | ISO 527-2/1A/5 | 2.5 | % |
|
|
彎曲模量 | 23°C | ASTM D790 | 8270 | ? MPa |
|
|
|
23°C | ISO 178 | 9700 | MPa |
|
|
彎曲強(qiáng)度 | 23°C | ASTM D790 | 193 | MPa |
|
|
|
23°C | ISO 178 | 210 | MPa |
|
|
簡支梁缺口沖擊強(qiáng)度 | -30°C | ISO 179/1eA | 8.5 | kJ/m2; |
| 熱性能 |
|
23°C | ISO 179/1eA | 8.5 | kJ/m2; |
|
|
簡支梁缺口沖擊強(qiáng)度 | -30°C | ISO 179/1eU | 45 | kJ/m2; |
|
|
|
23°C | ISO 179/1eU | 46 | kJ/m2; |
|
|
懸壁梁缺口沖擊強(qiáng)度 | 23°C | ASTM D256 | 91 | J/m |
|
|
|
23°C | ISO 180/1A | 7.5 | kJ/m2; |
|
|
熱變形溫度 | 0.45 MPa, 未退火 | ASTM D648 | 228 | °C |
|
|
|
0.45 MPa, 未退火 | ISO 75-2/B | 225 | ? °C |
|
|
|
1.8 MPa, 未退火 | ASTM D648 | 206 | °C |
|
|
|
1.8 MPa, 未退火 | ISO 75-2/A | 205 | ? °C |
|
|
|
8.0 MPa, 未退火 | ISO 75-2/C | 150 | °C |
|
|
玻璃轉(zhuǎn)化溫度 |
|
ISO 11357-2 | 60.0 | ? °C |
|
|
維卡軟化溫度 |
|
ISO 306/B50 | 220 | °C |
|
|
熔融溫度2 |
|
ISO 11357-3,ASTM D3418 | 225 | °C |
|
|
線形膨脹系數(shù) | 流動 | ISO 11359-2 | 0.000025 | cm/cm/°C |
|
|
|
橫向 | ISO 11359-2 | 0.00010 | cm/cm/°C |
| 電氣性能 | 表面電阻率 |
|
IEC 60093 | >1.0E+15 | ohms |
|
|
體積電阻率 | -- | ASTM D257 | 1.0E+15 | ohm.cm |
|
|
|
-- | IEC 60093 | >1.0E+15 | ohm.cm |
| 其它 | 介電強(qiáng)度 | --2 | ASTM D149 | 22 | KV/mm |
|
|
|
-- | IEC 60243-1 | 31 | ? KV/mm |
|
|
介電常數(shù) | 1 MHz | ASTM D150 | 3.70 |
|
|
|
|
100 Hz
|
IEC 60250 | 4.50 |
|
|
|
|
1 MHz | IEC 60250 | 4.10 |
|
|
|
耗散因數(shù) | 1 MHz | ASTM D150,IEC 60250 | 0.016 |
|
|
|
|
100Hz
|
IEC 60250 | 0.0022 |
|
|
|
漏電起痕指數(shù) | -- | IEC 60112 | 425 | V |
|
|
UL 阻燃等級 |
0.710 mm
|
UL 94 | HB |
|
|
|
極限氧指數(shù) |
?
|
ISO 4589-2 | 20 | % |